{"paper":{"title":"AC Loss and Contact Resistance In Copper-Stabilized Nb3Al Rutherford Cables with and without a Stainless Steel Core","license":"","headline":"","cross_cats":[],"primary_cat":"cond-mat.supr-con","authors_text":"A. Nijhuis, E. W. Collings, M.D. Sumption, R.M. Scanlan","submitted_at":"1999-11-12T14:14:21Z","abstract_excerpt":"Calorimetric measurements of AC loss and hence interstrand contact resistance (ICR), were measured on three samples of Rutherford cable wound with Cu-stabilized jelly-roll type unplated Nb3Al strand. One of the cable types was furnished with a thin core of AISI 316L stainless steel and the other two were both uncored but insulated in different ways. The cables were subjected to a room-temperature-applied uniaxial pressure of 12 MPa that was maintained during the reaction heat treatment (RHT), then vacuum impregnated with CTD 101 epoxy, and repressurized to 100 MPa during AC-loss measurement. T"},"claims":{"count":0,"items":[],"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"source":{"id":"cond-mat/9911191","kind":"arxiv","version":1},"verdict":{"id":null,"model_set":{},"created_at":null,"strongest_claim":"","one_line_summary":"","pipeline_version":null,"weakest_assumption":"","pith_extraction_headline":""},"references":{"count":0,"sample":[],"resolved_work":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57","internal_anchors":0},"formal_canon":{"evidence_count":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"author_claims":{"count":0,"strong_count":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"builder_version":"pith-number-builder-2026-05-17-v1"}