{"paper":{"title":"Full-Heusler Co2FeSi alloy thin films with perpendicular magnetic anisotropy induced by MgO-interface","license":"http://arxiv.org/licenses/nonexclusive-distrib/1.0/","headline":"","cross_cats":[],"primary_cat":"cond-mat.mtrl-sci","authors_text":"Shigeki Nakagawa, Takahiro Suzuki, Yorinobu Fujino, Yota Takamura","submitted_at":"2013-11-22T08:02:06Z","abstract_excerpt":"The authors demonstrated that L21-ordered full-Heusler Co2FeSi (CFS) alloy film with thickness of 100 nm were formed by facing targets sputtering (FTS) method at a substrate temperature TS = 300 deg C. Degrees of L21- and B2- order for the film were 0.37, and 0.96, respectively. Furthermore, full-Heusler CFS alloy thin films with perpendicular magnetic anisotropy (PMA) induced by MgO-interface magnetic anisotropy were successfully formed by the FTS method. The CFS/MgO stacking layers showed PMA when dCFS was 0.6 nm <= dCFS <= 1.0 nm. The PMA in these structures resulted from the CFS/MgO interf"},"claims":{"count":0,"items":[],"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"source":{"id":"1311.5670","kind":"arxiv","version":2},"verdict":{"id":null,"model_set":{},"created_at":null,"strongest_claim":"","one_line_summary":"","pipeline_version":null,"weakest_assumption":"","pith_extraction_headline":""},"references":{"count":0,"sample":[],"resolved_work":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57","internal_anchors":0},"formal_canon":{"evidence_count":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"author_claims":{"count":0,"strong_count":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"builder_version":"pith-number-builder-2026-05-17-v1"}