{"paper":{"title":"Crystal growth and characterization of Haldane chain compound Ni(C$_3$H$_{10}$N$_2$)$_2$NO$_2$ClO$_4$","license":"http://arxiv.org/licenses/nonexclusive-distrib/1.0/","headline":"","cross_cats":["cond-mat.mtrl-sci"],"primary_cat":"cond-mat.str-el","authors_text":"C. Fan, L. M. Chen, Q. J. Li, W. P. Ke, W. Tao, X. F. Sun (USTC), X. G. Liu, X. M. Wang, Z. Y. Zhao","submitted_at":"2013-11-12T06:12:23Z","abstract_excerpt":"The bulk single crystals of $S = 1$ chain compound Ni(C$_3$H$_{10}$N$_2$)$_2$NO$_2$ClO$_4$ are grown by using a slow evaporation method at a constant temperature and a slow cooling method. It is found that the optimum condition of growing large crystals is via slow evaporation at 25 $^\\circ$C using 0.015 mol Ni(ClO$_4$)$_2$$\\cdot$6H$_2$O, 0.015 mol NaNO$_2$, and 0.03 mol 1,3-propanediamine liquid dissolved into 30 ml aqueous solvent. High-quality crystals with size up to $18 \\times 7.5 \\times 5$ mm$^3$ are obtained. The single crystals are characterized by measurements of x-ray diffraction, ma"},"claims":{"count":0,"items":[],"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"source":{"id":"1311.2682","kind":"arxiv","version":1},"verdict":{"id":null,"model_set":{},"created_at":null,"strongest_claim":"","one_line_summary":"","pipeline_version":null,"weakest_assumption":"","pith_extraction_headline":""},"references":{"count":0,"sample":[],"resolved_work":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57","internal_anchors":0},"formal_canon":{"evidence_count":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"author_claims":{"count":0,"strong_count":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"builder_version":"pith-number-builder-2026-05-17-v1"}