{"paper":{"title":"Enhanced critical current properties in Ba0.6K0.4+xFe2As2 superconductor by over-doping of potassium","license":"http://arxiv.org/licenses/nonexclusive-distrib/1.0/","headline":"","cross_cats":[],"primary_cat":"cond-mat.supr-con","authors_text":"Chao Yao, Chunlei Wang, Dongliang Wang, Lei Wang, Xianping Zhang, Yanpeng Qi, Yanwei Ma, Zhaoshun Gao","submitted_at":"2011-01-28T02:06:19Z","abstract_excerpt":"Phase-pure polycrystalline Ba0.6K0.4+xFe2As2 with were prepared using a one-step solid-state reaction method. We found that over-doping of potassium can improve critical current density (Jc). High-field Jc for samples with x = 0.1 is three times higher than that for samples with x = 0. Over-doping of K has minimal effect on the critical transition temperature (Tc). Less than 0.5 K degradations in Tc was measured for samples with x = 0.1. TEM revealed high concentration of dislocations in samples with x = 0.1, resulting in enhanced flux pining. Further analyses on magnetization loops for powder"},"claims":{"count":0,"items":[],"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"source":{"id":"1101.5427","kind":"arxiv","version":1},"verdict":{"id":null,"model_set":{},"created_at":null,"strongest_claim":"","one_line_summary":"","pipeline_version":null,"weakest_assumption":"","pith_extraction_headline":""},"references":{"count":0,"sample":[],"resolved_work":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57","internal_anchors":0},"formal_canon":{"evidence_count":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"author_claims":{"count":0,"strong_count":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"builder_version":"pith-number-builder-2026-05-17-v1"}