{"paper":{"title":"Failure mechanisms of single-crystal silicon electrodes in lithium-ion batteries","license":"http://creativecommons.org/licenses/by/4.0/","headline":"","cross_cats":[],"primary_cat":"cond-mat.mtrl-sci","authors_text":"Feifei Shi, Gabor A. Somorjai, Kyriakos Komvopoulos, Philip N. Ross, Robert O. Ritchie, Zhichao Song","submitted_at":"2016-06-18T06:30:26Z","abstract_excerpt":"Long-term durability is a major obstacle limiting the widespread use of lithium ion batteries (LIBs) in heavy-duty applications and others demanding extended lifetime. As one of the root causes of degradation and failure of battery performance, the electrode failure mechanisms are still unknown. Here, we reveal the fundamental fracture mechanisms of single-crystal silicon electrodes over extended lithiation/delithiation cycles, using electrochemical testing, microstructure characterization, fracture mechanics, and finite element analysis. Anisotropic lithium invasion causes crack initiation pe"},"claims":{"count":0,"items":[],"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"source":{"id":"1606.06283","kind":"arxiv","version":1},"verdict":{"id":null,"model_set":{},"created_at":null,"strongest_claim":"","one_line_summary":"","pipeline_version":null,"weakest_assumption":"","pith_extraction_headline":""},"references":{"count":0,"sample":[],"resolved_work":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57","internal_anchors":0},"formal_canon":{"evidence_count":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"author_claims":{"count":0,"strong_count":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"builder_version":"pith-number-builder-2026-05-17-v1"}