{"paper":{"title":"Superconductivity in 1111-type CaFeAsF1-xHx induced by selective hydrogen elimination","license":"http://arxiv.org/licenses/nonexclusive-distrib/1.0/","headline":"","cross_cats":[],"primary_cat":"cond-mat.supr-con","authors_text":"Hideo Hosono, Taku Hanna Yoshinori Muraba Satoru Matsuishi","submitted_at":"2013-09-25T04:05:19Z","abstract_excerpt":"The difference in thermal stability of F- and H- in 1111-type iron based superconductors, allows selective hydrogen elimination from non-superconductive CaFeAsF0.8H0.2 by thermal annealing. The analyzed chemical composition of the resulting samples indicates that incorporated hydrogen was selectively eliminated by thermal annealing at 553 K for 72 hours. The resulting hydrogen-eliminated sample shows bulk superconductivity with Tc = 29 K. This technique may be used for indirect electron doping for AeFeAeF (Ae; alkali-earth metal) iron based superconductor described by CaFeAsF1-xHx => CaFeAsF1-"},"claims":{"count":0,"items":[],"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"source":{"id":"1309.6398","kind":"arxiv","version":2},"verdict":{"id":null,"model_set":{},"created_at":null,"strongest_claim":"","one_line_summary":"","pipeline_version":null,"weakest_assumption":"","pith_extraction_headline":""},"references":{"count":0,"sample":[],"resolved_work":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57","internal_anchors":0},"formal_canon":{"evidence_count":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"author_claims":{"count":0,"strong_count":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"builder_version":"pith-number-builder-2026-05-17-v1"}