Boron doping broadens the stability window of Cu2O and Cu4O3 phases in reactive-sputtered Cu-O films, delaying the shift to CuO and enabling resistivities as low as 0.06 Ω cm in mixed-valence regimes.
Thermodynamic Properties of Minerals and Related Substances at 298.15 K and 1 Bar ( 10^5 Pascals) Pressure and at Higher Temperatures
1 Pith paper cite this work. Polarity classification is still indexing.
1
Pith paper citing it
fields
cond-mat.mtrl-sci 1years
2026 1verdicts
UNVERDICTED 1representative citing papers
citing papers explorer
-
Boron-assisted stabilization of low-resistivity mixed-valence Cu-O thin films prepared by reactive magnetron sputtering
Boron doping broadens the stability window of Cu2O and Cu4O3 phases in reactive-sputtered Cu-O films, delaying the shift to CuO and enabling resistivities as low as 0.06 Ω cm in mixed-valence regimes.