InAs nanofins grown by dielectric-templated selective area epitaxy can be mechanically transferred and fabricated into multi-contact Hall devices showing 3D electron densities of 2.5-5e17 cm^-3, Hall mobilities up to 1200 cm2/Vs, field-effect mobilities up to 4400 cm2/Vs, and quantum interference up
and Palmstrøm, C.J., Selective-area chemical beam e pitaxy on in-plane InAs one-dimensional channels grown on InP(001) and InP(111)B surfaces, arXiv: 1808.04563 (2018)
1 Pith paper cite this work. Polarity classification is still indexing.
1
Pith paper citing it
fields
cond-mat.mes-hall 1years
2019 1verdicts
UNVERDICTED 1representative citing papers
citing papers explorer
-
Regaining a spatial dimension: Mechanically transferrable two-dimensional InAs nanofins grown by selective area epitaxy
InAs nanofins grown by dielectric-templated selective area epitaxy can be mechanically transferred and fabricated into multi-contact Hall devices showing 3D electron densities of 2.5-5e17 cm^-3, Hall mobilities up to 1200 cm2/Vs, field-effect mobilities up to 4400 cm2/Vs, and quantum interference up