Higher currents enhance spin alignment at grain boundaries in polycrystalline NiCo2O4 via spin injection, shifting transport from semiconducting hopping to more metallic conduction.
Powder diffraction file no. 471049,
1 Pith paper cite this work. Polarity classification is still indexing.
1
Pith paper citing it
fields
cond-mat.mtrl-sci 1years
2026 1verdicts
UNVERDICTED 1representative citing papers
citing papers explorer
-
Spin-related transport in a polycrystalline NiCo2O4 film: Drastic current-induced change in resistivity-temperature characteristics via spin injection
Higher currents enhance spin alignment at grain boundaries in polycrystalline NiCo2O4 via spin injection, shifting transport from semiconducting hopping to more metallic conduction.