A spin reorientation transition in Pt/Co/molecular heterostructures, tunable near room temperature, can be triggered by modest current density or femtosecond laser pulses.
The (111) textured Pt layers of ≈4 nm thickness (Figure S24, Supporting Information, shows the XRD peak) were grown at 500 °C with e-beam evaporation at a growth rate of ≈0.1Ȧ/s