The 60CPO-40PSFAO dual-phase membrane reaches 1.03 mL cm^{-2} min^{-1} oxygen flux at 1000°C with phase stability in CO2 for over 100 h.
Title resolution pending
2 Pith papers cite this work. Polarity classification is still indexing.
2
Pith papers citing it
fields
physics.app-ph 2years
2019 2verdicts
UNVERDICTED 2representative citing papers
Al doping in 60CPO-40PSF dual-phase membranes optimizes oxygen permeability at x=0.4 with a rate of 1.12 mL min^{-1} cm^{-2} at 1000°C while preserving stability.
citing papers explorer
-
High CO2-tolerance oxygen permeation dual-phase membranes Ce0.9Pr0.1O2-{\delta}-Pr0.6Sr0.4Fe0.8Al0.2O3-{\delta}
The 60CPO-40PSFAO dual-phase membrane reaches 1.03 mL cm^{-2} min^{-1} oxygen flux at 1000°C with phase stability in CO2 for over 100 h.
-
Effects of Al content on the oxygen permeability through dual-phase membrane 60Ce$_{0.9}$Pr$_{0.1}$O$_{2-\delta}$-40Pr$_{0.6}$Sr$_{0.4}$Fe$_{1-x}$Al$_x$O$_{3-\delta}$
Al doping in 60CPO-40PSF dual-phase membranes optimizes oxygen permeability at x=0.4 with a rate of 1.12 mL min^{-1} cm^{-2} at 1000°C while preserving stability.