Jahn-Teller effect and stability of the charge-ordered state in La1-xCaxMnO3 (0.5<x<0.9) manganites

The longitudinal ultrasonic sound velocity and attenuation, the resistivity, and lattice parameters were studied as a function of temperature from 30 K to 300 K in La1-xCaxMnO3 (0.5<x<0.9). For all the samples, a dramatic stiffening of the sound velocity below the charge ordering transition temperature TCO was directly driven by distinct changes of the lattice parameters due to the formation of long range ordering of Jahn-Teller distorted MnO6 octahedra. The relative change of the sound velocity (DeltaV/V) below TCO depends on the Ca concentration x and reaches the maximum at x=0.75, implying that the effective strength of electron-lattice interaction with the Jahn-Teller distortion is the strongest at x=0.75 and hence the charge ordered state is mostly stabilized near x=0.75 and insensitive to the application of a magnetic field, which is supported by the charge transport properties under high magnetic fields up to 14T.