First 3D reconstruction of dislocations in β-Ga₂O₃ via Borrmann-effect X-ray topo-tomography.
Title resolution pending
2 Pith papers cite this work. Polarity classification is still indexing.
2
Pith papers citing it
citation-role summary
background 1
citation-polarity summary
fields
cond-mat.mtrl-sci 2years
2026 2verdicts
UNVERDICTED 2roles
background 1polarities
background 1representative citing papers
X-ray topography shows high crystalline quality (26 arcsec FWHM) beneath the seed in OCCC-grown β-Ga2O3 with <010> screw dislocations at ~10^5 cm^{-2} and twist misorientation during diameter enlargement.
citing papers explorer
-
Three-dimensional visualization of lattice defects in $\beta$-Ga$_2$O$_3$ via synchrotron-radiation Borrmann-effect X-ray topo-tomography
First 3D reconstruction of dislocations in β-Ga₂O₃ via Borrmann-effect X-ray topo-tomography.
-
Synchrotron-radiation X-ray topography and reticulography of bulk $\beta$-Ga$_2$O$_3$ crystals grown by the cold crucible method
X-ray topography shows high crystalline quality (26 arcsec FWHM) beneath the seed in OCCC-grown β-Ga2O3 with <010> screw dislocations at ~10^5 cm^{-2} and twist misorientation during diameter enlargement.