Diffusion-induced grain boundary migration is the dominant mechanism for rapid Cr dealloying and porosity formation in Ni-30Cr during molten chloride salt exposure, with surface-induced grain structure dictating the corrosion morphology.
Lyon, 1 - Overview of corrosion engineering, science and technology, in: D
1 Pith paper cite this work. Polarity classification is still indexing.
1
Pith paper citing it
citation-role summary
background 1
citation-polarity summary
fields
cond-mat.mtrl-sci 1years
2026 1verdicts
CONDITIONAL 1roles
background 1polarities
background 1representative citing papers
citing papers explorer
-
Role of diffusion-induced grain boundary migration during molten salt corrosion of a Ni-30Cr alloy
Diffusion-induced grain boundary migration is the dominant mechanism for rapid Cr dealloying and porosity formation in Ni-30Cr during molten chloride salt exposure, with surface-induced grain structure dictating the corrosion morphology.