Precipitate-induced dynamic strain aging arising from nearest-neighbor Cu-Al exchanges at dislocations produces low strain-rate sensitivity across intermediate quasi-static rates in precipitation-hardened aluminum alloys.
Pipe-diffusion ripening of si precipitates in al-0.5% cu-1% si thin films.Philosophical Magazine, 85(30):3541–3552