Precipitate-induced dynamic strain aging arising from nearest-neighbor Cu-Al exchanges at dislocations produces low strain-rate sensitivity across intermediate quasi-static rates in precipitation-hardened aluminum alloys.
Aluminum alloys with iden- tical plastic flow and different strain rate sensitivity.Metallurgical and Materials Transactions A, 41(13):3358–3364