Epitaxial L2_1-ordered Co2MnSi waveguides exhibit intrinsic cubic magnetocrystalline anisotropy that suppresses first-order nonlinear instabilities over several GHz at zero bias and stabilizes low-bias Damon-Eshbach operation.