GaMnN epitaxial films with high magnetization

We report on the fabrication of pseudomorphic wurtzite GaMnN grown on GaN with Mn concentrations up to 10% using molecular beam epitaxy. According to Rutherford backscattering the Mn ions are mainly at the Ga-substitutional positions, and they are homogeneously distributed according to depth-resolved Auger-electron spectroscopy and secondary-ion mass-spectroscopy measurements. A random Mn distribution is indicated by transmission electron microscopy, no Mn-rich clusters are present for optimized growth conditions. A linear increase of the c-lattice parameter with increasing Mn concentration is found using x-ray diffraction. The ferromagnetic behavior is confirmed by superconducting quantum-interference measurements showing saturation magnetizations of up to 150 emu/cm^3.