Evolution of optical properties of chromium spinels CdCr₂O₄, HgCr₂S₄, and ZnCr₂Se₄ under high pressure

We report pressure-dependent reflection and transmission measurements on ZnCr$_2$Se$_4$, HgCr$_2$S$_4$, and CdCr$_2$O$_4$ single crystals at room temperature over a broad spectral range 200-24000 cm$^{-1}$. The pressure dependence of the phonon modes and the high-frequency electronic excitations indicates that all three compounds undergo a pressure-induced structural phase transition with the critical pressure 15 GPa, 12 GPa, and 10 GPa for CdCr$_2$O$_4$, HgCr$_2$S$_4$, and ZnCr$_2$Se$_4$, respectively. The eigenfrequencies of the electronic transitions are very close to the expected values for chromium crystal-field transitions. In the case of the chalcogenides pressure induces a red shift of the electronic excitation which indicates a strong hybridization of the Cr d-bands with the chalcogenide bands.