Bulk Superconductivity in Fe1+yTe0.6Se0.4 Induced by Removal of Excess Fe

Experimental evidences from transport, magnetic, and magneto-optical (MO) image measurements confirmed that arsenic (As) vapor annealing was another effective way to induce bulk superconductivity with isotropic, large, and homogenous superconducting critical current density (Jc) in Fe1+yTe0.6Se0.4 single crystal. Since As is an exotic and easily detectable heavy element to Fe1+yTe0.6Se0.4 single crystal, As vapor annealing is very advantageous for the study of annealing mechanism. Detailed micro-structural and elemental analyses exclude the possibility that intercalating or doping effect may happen in the other post-annealing methods, proving that Fe reacts with As on the surface of the crystal and the reaction itself acts as a driving force to drag excess Fe out. The removal of excess Fe results in the good superconductivity performance.