A coupling of martensitic and metamagnetic transitions with collective magneto-volume and table-like magnetocaloric effects

A coupling of the first-order paramagnetic-to-induced-ferromagnetic martensitic and the second-order antiferromagnetic-to-ferromagnetic metamagnetic transitions was found in MnNi0.8Fe0.2Ge alloy. Based on the coupling, a magneto-volume effect driven by the martensitic transition and a table-like magnetocaloric effect generated by the successive magnetic phase transitions arise collectively. By using the magneto-volume effect, the internal pressure stress in the volume-expansion martensitic transition was determined at 350 MPa. The magnetocaloric effect, with a wide working temperature range of 26 K around room temperature, shows a small hysteresis loss (5 J/kg) and a large net refrigerant capacity (157 J/kg).