Polar compensation at the surface of SrTiO3 (111)

We have systematically investigated the annealing effect on the structure and composition of the polar surface of SrTiO3 (111), starting with an ex-situ chemical etch. The relative surface concentration between Ti and Sr strongly depends on both the annealing temperature and the oxygen processing. There is a critical annealing temperature at which the maximum concentration ratio of Ti to Sr is achieved, while still maintaining a (1 x 1) surface structure. We demonstrate that with proper processing it is possible to avoid surface reconstruction over a broad temperature range. Our results provide an optimal temperature window for epitaxial film growth.