Fabrication of grain boundary junctions using NdFeAs(O,F) superconducting thin films

We report on the growth of NdFeAs(O,F) thin films on [001]-tilt MgO bicrystal substrates with misorientation angle theta_GB=6{\deg}, 12{\deg}, 24{\deg} and 45{\deg}, and their inter- and intra-grain transport properties. X-ray diffraction study confirmed that all our NdFeAs(O,F) films are epitaxially grown on the MgO bicrystals. The theta_GB dependence of the inter-grain critical current density Jc shows that, unlike Co-doped BaFe2As2 and Fe(Se,Te), its decay with theta_GB is rather significant. As a possible reason of this result, fluorine may have diffused preferentially to the grain boundary region and eroded the crystal structure.