On the segregation of Re at dislocations in the {γ}' phase of Ni-based single crystal superalloys

We report evidence of Re and Mo segregation (up to 2.6 at.% and 1 at.%) along with Cr and Co to the dislocations inside of {\gamma}' precipitates in a second generation Ni-based single crystal superalloy, after creep deformation at 750{\deg}C under an applied stress of 800 MPa. The observed segregation effects can be rationalized through bridging the solute partitioning behavior across the {\gamma}/{\gamma}' interface and the pipe diffusion mechanism along the core of the dislocation line. This understanding can provide new insights enabling improved alloy design.