Revisiting the phase diagram of T*-type La_(1-x/2)Eu_(1-x/2)Sr_xCuO₄ using Oxygen K-edge X-ray absorption spectroscopy

Oxygen $K$-edge X-ray absorption spectroscopy measurements were conducted on T*-type La$_{1-x/2}$Eu$_{1-x/2}$Sr$_x$CuO$_4$ (LESCO) to estimate the hole density ($n_{\rm h}$) and investigate the oxidation annealing effect on $n_{\rm h}$. A drastic increase in $n_{\rm h}$ due to annealing was found. The increase in $n_{\rm h}$ cannot be explained solely by the oxygen gain due to annealing, suggesting that delocalized holes are introduced into the CuO$_2$ plane. A phase diagram of LESCO was redrawn against $n_{\rm h}$.