High transport currents in mechanically reinforced MgB2 wires

We prepared and characterized monofilamentary MgB2 wires with a mechanically reinforced composite sheath of Ta(Nb)/Cu/steel, which leads to dense filaments and correspondingly high transport currents up to Jc = 10^5 A/cm^2 at 4.2 K, self field. The reproducibility of the measured transport currents was excellent and not depending on the wire diameter. Using different precursors, commercial reacted powder or an unreacted Mg/B powder mixture, a strong influence on the pinning behaviour and the irreversibility field was observed. The critical transport current density showed a nearly linear temperature dependency for all wires being still 52 kA/cm^2 at 20 K and 23 kA/cm^2 at 30 K. Detailed data for Jc(B,T) and Tc(B) were measured.