Semiconductive and Photoconductive Properties of the Single Molecule Magnets Mn₁₂-Acetate and Fe₈Br₈

Resistivity measurements are reported for single crystals of Mn$_{12}$-Acetate and Fe$_8$Br$_8$. Both materials exhibit a semiconductor-like, thermally activated behavior over the 200-300 K range. The activation energy, $E_a$, obtained for Mn$_{12}$-Acetate was 0.37 $\pm$ 0.05 eV, which is to be contrasted with the value of 0.55 eV deduced from the earlier reported absorption edge measurements and the range of 0.3-1 eV from intramolecular density of states calculations, assuming $2E_a$= $E_g$, the optical band gap. For Fe$_8$Br$_8$, $E_a$ was measured as 0.73 $\pm$ 0.1 eV, and is discussed in light of the available approximate band structure calculations. Some plausible pathways are indicated based on the crystal structures of both lattices. For Mn$_{12}$-Acetate, we also measured photoconductivity in the visible range; the conductivity increased by a factor of about eight on increasing the photon energy from 632.8 nm (red) to 488 nm (blue). X-ray irradiation increased the resistivity, but $E_a$ was insensitive to exposure.