Entropy change at the martensitic transformation in ferromagnetic shape memory alloys Ni_(2+x)Mn_(1-x)Ga

The entropy change $\Delta S$ between the high-temperature cubic phase and the low-temperature tetragonally-based martensitic phase of Ni$_{2+x}$Mn$_{1-x}$Ga ($x = 0 - 0.20$) alloys was studied. The experimental results obtained indicate that $\Delta S$ in the Ni$_{2+x}$Mn$_{1-x}$Ga alloys increases with the Ni excess $x$. The increase of $\Delta S$ is presumably accounted for by an increase of magnetic contribution to the entropy change. It is suggested that the change in modulation of the martensitic phase of Ni$_{2+x}$Mn$_{1-x}$Ga results in discontinuity of the composition dependence of $\Delta S$.