Magnetic Phase Diagram of GdNi2B2C: Two-ion Magnetoelasticity and Anisotropic Exchange Couplings

Extensive magnetization and magnetostriction measurements were carried out on a single crystal of GdNi2B2C along the main tetragonal axes. Within the paramagnetic phase, the magnetic and strain susceptibilities revealed a weak anisotropy in the exchange couplings and two-ion tetragonal-preserving alpha-strain modes. Within the ordered phase, magnetization and magnetostriction revealed a relatively strong orthorhombic distortion mode and rich field-temperature phase diagrams. For H//(100) phase diagram, three field-induced transformations were observed, namely, at: Hd(T), related to the domain alignment; Hr(T), associated with reorientation of the moment towards the c-axis; and Hs(T), defining the saturation process wherein the exchange field is completely counterbalanced. On the other hand, For H//(001) phase diagram, only two field-induced transformations were observed, namely at: Hr(T) and Hs(T). For both phase diagrams, Hs(T) follows the relation Hs[1-(T/Tn)^2]^(1/2)kOe with Hs(T-->0)=128.5(5) kOe and Tn(H=0)=19.5 K. In contrast, the thermal evolution of Hr(T) along the c-axis (much simpler than along the a-axis) follows the relation Hr[1-T/Tr]^(1/3) kOe where Hr(T-->0)=33.5(5) kOe and Tr(H=0)=13.5 K. It is emphasized that the magnetoelastic interaction and the anisotropic exchange coupling are important perturbations and therefore should be explicitly considered if a complete analysis of the magnetic properties of the borocarbides is desired.