High Pressure Study of Structural Phase Transitions and Superconductivity in La1.48Nd0.4Sr0.12CuO4

We have determined the crystal structures and superconducting transition temperatures of La1.48Nd0.4Sr0.12CuO4 under nearly hydrostatic pressures in diamond anvil cells to 5.0 GPa and 19.0 GPa, respectively. Synchrotron x-ray powder diffraction measurements were used to establish the pressure-temperature structural phase diagram. Under pressure the superconducting transition temperature increases rapidly from Tc = 3 K to a maximum value of 22 K at 5 GPa, a pressure slightly greater than that required to stabilize the undistorted I4/mmm structure in the superconducting state. Increasing the pressure further to 19 GPa leads to a decrease in Tc to ~12 K. These results are discussed in relation to earlier high pressure measurements for similar materials.