3D-Hydrogen Analysis of Ferromagnetic Microstructures in Proton Irradiated Graphite

Recently, magnetic order in highly oriented pyrolytic graphite (HOPG) induced by proton broad- and microbeam irradiation was discovered. Theoretical models propose that hydrogen could play a major role in the magnetism mechanism. We analysed the hydrogen distribution of pristine as well as irradiated HOPG samples, which were implanted to micrometer-sized spots as well as extended areas with various doses of 2.25 MeV protons at the Leipzig microprobe LIPSION. For this we used the sensitive 3D hydrogen microscopy system at the Munich microprobe SNAKE. The background hydrogen level in pristine HOPG is determined to be less than 0.3 at-ppm. About 4.8e15 H-atoms/cm^2 are observed in the near-surface region (4 um depth resolution). The depth profiles of the implants show hydrogen located within a confined peak at the end of range, in agreement with SRIM Monte Carlo simulations, and no evidence of diffusion broadening along the c-axis. At sample with microspots, up to 40 at-% of the implanted hydrogen is not detected, providing support for lateral hydrogen diffusion.