Shape Transition in the Epitaxial Growth of Gold Silicide in Au Thin Films on Si(111)

Growth of epitaxial gold silicide islands on bromine-passivated Si(111) substrates has been studied by optical and electron microscopy, electron probe micro analysis and helium ion backscattering. The islands grow in the shape of equilateral triangles up to a critical size beyond which the symmetry of the structure is broken, resulting in a shape transition from triangle to trapezoid. The island edges are aligned along $Si[110]$ directions. We have observed elongated islands with aspect ratios as large as 8:1. These islands, instead of growing along three equivalent [110] directions on the Si(111) substrate, grow only along one preferential direction. This has been attributed to the vicinality of the substrate surface.