The Doping Phase Diagram of Y1-xcaxba2(Cu1-yzny)3O7-d from Transport Measurements: Tracking the Pseudogap Below Tc (y = 0)

The effects of planar hole concentration, p, on the resistivity, r(T), of sintered Y1-xCaxBa2(Cu1-yZny)3O7-d samples were investigated over a wide range of Ca, Zn, and oxygen contents. Zn was used to suppress superconductivity and this enabled us to extract the characteristic pseudogap temperature, T*(p), from r(T,p) data below Tco(p) [ = Tc (y = 0)]. We have also located the characteristic temperature, Tscf, marking the onset of significant superconducting fluctuations above Tc, from the analysis of r(T,H,p) and r(T,p) data. This enabled us to identify T*(p) near the optimum doping level where the values of T*(p) and Tscf(p) are very close and hard to distinguish. We again found that T*(p) depends only on the hole concentration p, and not on the level of disorder associated with Zn or Ca substitutions. We conclude that (i) T*(p) (and therefore, the pseudogap) persists below Tco(p) on the overdoped side and does not merge with the Tco(p) line and (ii) T*(p), and thus the pseudogap energy, extrapolates to zero at the doping p = 0.19 +/- 0.01. PACS numbers: 74.25.Dw, 74.25. 74.62.Dh, 74.72.-h Key words: Pseudoap, Superconducting fluctuations