Crystallography and Physical Properties of BaCo2As2, Ba{0.94}K{0.06}Co2As2 and Ba{0.78}K{0.22}Co2As2

The crystallographic and physical properties of polycrystalline and single crystal samples of BaCo2As2 and K-doped Ba{1-x}K{x}Co2As2 (x = 0.06, 0.22) are investigated by x-ray and neutron powder diffraction, magnetic susceptibility chi, magnetization, heat capacity Cp, {75}As NMR and electrical resistivity rho measurements versus temperature T. The crystals were grown using both Sn flux and CoAs self-flux, where the Sn-grown crystals contain 1.6-2.0 mol% Sn. All samples crystallize in the tetragonal ThCr2Si2-type structure (space group I4/mmm). For BaCo2As2, powder neutron diffraction data show that the c-axis lattice parameter exhibits anomalous negative thermal expansion from 10 to 300 K, whereas the a-axis lattice parameter and the unit cell volume show normal positive thermal expansion over this T range. No transitions in BaCo2As2 were found in this T range from any of the measurements. Below 40-50 K, we find rho ~ T^2 indicating a Fermi liquid ground state. A large density of states at the Fermi energy D(EF) ~ 18 states/(eV f.u.) for both spin directions is found from low-T Cp(T) measurements, whereas the band structure calculations give D(EF) = 8.23 states/(eV f.u.). The {75}As NMR shift data versus T have the same T dependence as the chi(T) data, demonstrating that the derived chi(T) data are intrinsic. The observed {75}As nuclear spin dynamics are consistent with the presence of ferromagnetic and/or stripe-type antiferromagnetic spin fluctuations. The crystals of Ba{0.78}K{0.22}Co2As2 were grown in Sn flux and show properties very similar to those of undoped BaCo2As2. On the other hand, the crystals from two batches of Ba{0.94}K{0.06}Co2As2 grown in CoAs self-flux show evidence of weak ferromagnetism at T < 10 K with small ordered moments at 1.8 K of 0.007 and 0.03 muB per formula unit, respectively.