Impedance spectroscopy studies on lead free Ba_(1-x)Mg_x(Ti0_(.9)Zr_(0.1))O₃ ceramics

Ba1-xMgx(Ti0.9Zr0.1)O3(x= 0.01 and 0.02) ceramics were prepared using the conventional solid state reaction. Rietveld refinement performed on X-ray diffraction patterns indicates that the samples are tetragonal crystal structure with P4mm space group. By increasing Mg content from 1 to 2% the unit cell volume decreased. Likewise, the grains size is greatly reduced from 10 to 4 micrometer. The temperature dependence of dielectric constants at different frequencies exhibited typical relaxor ferroelectric characteristic, with sensitive dependence in frequency and temperature for ac conductivity. The obtained activation energy values were correlated to the proposed conduction mechanisms.