Transport critical current of Solenoidal MgB2/Cu Coils Fabricated Using a Wind-Reaction In-situ Technique

In this letter, we report the results of transport Jc of solenoid coils upto 100 turns fabricated with Cu-sheathed MgB2 wires using a wind-reaction in-situ technique. Despite the low density of single core and some reaction between Mg and Cu-sheath, our results demonstrate the decrease in transport Jc with increasing length of MgB2 wires is insignificant. Solenoid coils with diameter as small as 10 mm can be readily fabricated using a wind-reaction in-situ technique. The Jc of coils is essentially the same as in the form of straight wires. A Jc of 133,000 A/cm2 and 125,000 A/cm2 at 4 K and self field has been achieved for a small coil wound using Cu-sheathed tape and Cu-sheathed wire respectively. These results indicate that the MgB2 wires have a great potential for lage scale applications