Development of high critical current density in multifilamentary round-wire Bi2Sr2CaCu2O8+x by strong overdoping

Bi2Sr2CaCu2O8+x is the only cuprate superconductor that can be made into a round-wire conductor form with a high enough critical current density Jc for applications. Here we show that the Jc(5 T,4.2 K) of such Ag-sheathed filamentary wires can be doubled to more than 1.4x10^5 A/cm^2 by low temperature oxygenation. Careful analysis shows that the improved performance is associated with a 12 K reduction in transition temperature Tc to 80 K and a significant enhancement in intergranular connectivity. In spite of the macroscopically untextured nature of the wire, overdoping is highly effective in producing high Jc values.