Temperature and misorientation-dependent austenite nucleation at ferrite grain boundaries in a medium manganese steel: role of misorientation-dependent grain boundary segregation

In the current work, we study the role of grain boundary (GB) misorientation-dependent segregation on austenite nucleation in a 50% cold rolled intercritically annealed 10Mn-0.05C-1.5Al (wt. %) medium Mn steel. During intercritical annealing at 500{\deg}C, austenite nucleates predominantly at high-angle GBs. At 600{\deg}C, austenite nucleates additionally at low-angle GBs, exhibiting a temperature dependance. Correlative transmission Kikuchi diffraction /atom probe tomography reveals a misorientation-dependent segregation. While GB segregation has been reported to assist austenite nucleation in medium manganese steels (3-12 wt.% Mn), an understanding of the temperature and misorientation dependance is lacking, which is the aim of current work. Since artifacts of atom probe can cause a broadening of the segregation width, we combined experiments with results from density functional theory (DFT) calculations that reveal that the Mn segregation is not limited to the GB plane but confined to a region in the range of approximately 1 nm. Consequently, GB segregation alters both the GB interface energy and the free energy per unit volume corresponding to the transformation. We estimate the local driving force for austenite nucleation accounting for the segregation width of ~ 1 nm. Based on classical nucleation theory, we clarify the effect of GB segregation on the critical radius and activation energy barrier for confined austenite nucleation at the GB.