Evidence of Hot Carrier Extraction in Metal Halide Perovskite Solar Cells

The presence of hot carriers is presented in the operational properties of an (FA,Cs)Pb(I, Br, Cl)3 solar cell at ambient temperatures and under practical solar concentration. At 100 K, clear evidence of hot carriers is observed in both the high energy tail of the photoluminescence spectra and from the appearance of a non-equilibrium photocurrent at higher fluence in light J-V measurements. At room temperature, however, the presence of hot carriers in the emission at elevated laser fluence are shown to compete with a gradual red shift in the PL peak energy as photo induced halide segregation begins to occur at higher lattice temperature. The effects of thermionic emission of hot carriers and the presence of a non-equilibrium carrier distribution are also shown to be distinct from simple lattice heating. This results in large unsaturated photocurrents at high powers as the Fermi distribution exceeds that of the heterointerface controlling carrier transport and rectification.