arxiv: 2605.21767 · v1 · pith:HVV4OB2Cnew · submitted 2026-05-20 · ❄️ cond-mat.mtrl-sci

Uncovering Antipolar Ordering and Pressure-Tunable Phases in Hexagonal LaN

Atanu Paul , Laurent Bellaiche , Charles Paillard This is my paper

Pith reviewed 2026-05-22 08:19 UTC · model grok-4.3

classification ❄️ cond-mat.mtrl-sci
keywords antipolar orderinghexagonal LaNwurtzite phasepressure tuningphonon instabilityfirst-principlesbinary nitride
0
0 comments X

The pith

LaN hosts a metastable antipolar hexagonal phase whose barrier to the polar wurtzite structure shrinks under pressure.

A machine-rendered reading of the paper's core claim, the machinery that carries it, and where it could break.

The work applies density functional theory to a nonpolar hexagonal starting structure of LaN and finds two competing soft phonon modes at the zone center. One mode is polar and relaxes into the familiar wurtzite lattice; the other is antipolar and produces a new hexagonal phase in which local dipoles alternate so that the net cell polarization is zero. At ambient pressure this antipolar phase lies above the wurtzite ground state but is separated from it by a finite barrier. That barrier falls steadily with increasing pressure, while the local polarization inside the antipolar phase grows. At still higher pressures the rock-salt and tetragonal structures overtake both hexagonal phases.

Core claim

Starting from the nonpolar hexagonal phase of LaN, first-principles density functional theory identifies competing polar and antipolar zone-center phonon instabilities. Condensation of the antipolar mode stabilizes a dynamically stable hexagonal antipolar phase characterized by alternating local polarization and zero net macroscopic polarization within the unit cell. At ambient conditions the antipolar phase is metastable with respect to the wurtzite phase, yet a finite energy barrier separates the two, and this barrier decreases with increasing pressure.

What carries the argument

Condensation of the antipolar zone-center phonon mode that yields an hexagonal antipolar phase with alternating local polarizations and zero net macroscopic polarization.

If this is right

  • The antipolar phase supplies a possible intermediate state for polarization reversal between opposite wurtzite orientations.
  • Pressure simultaneously lowers the barrier and increases the sublattice polarization inside the antipolar phase while decreasing it inside the wurtzite phase.
  • Hexagonal phases remain competitive only in the low-pressure window; above a threshold the rock-salt and tetragonal structures become lower in energy.
  • Pressure therefore offers a practical knob for switching between polar and antipolar order in this binary nitride.

Where Pith is reading between the lines

These are editorial extensions of the paper, not claims the author makes directly.

  • The same antipolar instability may appear in other hexagonal nitrides and could be located by analogous phonon calculations.
  • Dielectric or diffraction experiments performed under hydrostatic pressure on LaN would directly test the predicted barrier reduction and phase competition.

Load-bearing premise

The relative energies of the phases and the frequencies of the soft modes are taken from density-functional calculations whose quantitative accuracy for LaN has not been cross-checked against experiment or higher-level theory.

What would settle it

Observation of the antipolar phase at low pressure or a direct measurement showing that the energy barrier between wurtzite and antipolar phases fails to decrease with pressure.

Figures

Figures reproduced from arXiv: 2605.21767 by Atanu Paul, Charles Paillard, Laurent Bellaiche.

Figure 1
Figure 1. Figure 1: FIG. 1. LaN-H5: (a) Unit cell containing La (green) and [PITH_FULL_IMAGE:figures/full_fig_p002_1.png] view at source ↗
Figure 2
Figure 2. Figure 2: FIG. 2. LaN-AP: (a) Unit cell containing La (green) and N [PITH_FULL_IMAGE:figures/full_fig_p003_2.png] view at source ↗
Figure 4
Figure 4. Figure 4: FIG. 4. (a) Enthalpy of the WZ and AP phases with applied [PITH_FULL_IMAGE:figures/full_fig_p003_4.png] view at source ↗
Figure 3
Figure 3. Figure 3: FIG. 3. (a) Energy with axial ratio for the linearly interpo [PITH_FULL_IMAGE:figures/full_fig_p003_3.png] view at source ↗
read the original abstract

We predict an antipolar instability in hexagonal LaN using first-principles density functional theory. Starting from a nonpolar hexagonal phase, we identify competing polar and antipolar zone-center phonon instabilities. Condensation of the polar and antipolar modes stabilizes, respectively, dynamically stable wurtzite (WZ) phase and an hexagonal antipolar (AP) phase which is characterized by alternating local polarization and zero net macroscopic polarization within the unit cell. At ambient conditions, the AP phase is metastable with respect to the WZ phase, and a finite energy barrier exists between these phases, suggesting a possible polarization-switching pathway via the AP intermediate state. The energy barrier between the WZ and AP phases decreases with increasing pressure, indicating enhanced tunability between polar and antipolar states. The sublattice polarization increases with pressure in the AP phase, while it decreases in the WZ phase. We further find that, with increasing pressure, the rock-salt and tetragonal phases of LaN become more stable than the hexagonal phases (AP and WZ). Consequently, the realization of the AP phase is more favorable in the low-pressure regime, where hexagonal phases remain energetically competitive. These results demonstrate pressure-driven competition between polar and antipolar phases in LaN and point toward antiferroelectric-like behavior in this binary nitride system.

Editorial analysis

A structured set of objections, weighed in public.

Desk editor's note, referee report, simulated authors' rebuttal, and a circularity audit. Tearing a paper down is the easy half of reading it; the pith above is the substance, this is the friction.

Referee Report

2 major / 1 minor

Summary. The manuscript uses first-principles DFT to predict competing polar and antipolar zone-center phonon instabilities in hexagonal LaN. Condensation of the antipolar mode produces a dynamically stable hexagonal antipolar (AP) phase with zero net polarization, while the polar mode yields the wurtzite (WZ) structure. At ambient pressure the AP phase is metastable relative to WZ with a finite energy barrier; this barrier decreases with pressure while the rock-salt and tetragonal phases become energetically favored at higher pressures.

Significance. If the underlying DFT energetics and phonon spectra prove robust, the work identifies a pressure-tunable polar–antipolar competition in a binary nitride together with a possible polarization-switching pathway through the AP intermediate. Such results would be of interest for antiferroelectric-like behavior in nitride systems and for pressure-controlled phase engineering.

major comments (2)
  1. [Computational Methods] Computational Methods section: the exchange-correlation functional, k-point mesh, plane-wave cutoff, and convergence tolerances used for the phonon and total-energy calculations are not reported. Because relative energies between hexagonal and cubic LaN phases are known to shift by tens of meV/atom when changing from PBE to LDA or hybrid functionals, and because soft-mode frequencies can change sign under the same change, the claimed dynamical stability of the AP phase and the finite WZ–AP barrier cannot be assessed without these controls.
  2. [Results] Results on phase energetics and pressure dependence: the metastability of AP with respect to WZ, the pressure-induced closure of the WZ–AP barrier, and the crossover to rock-salt/tetragonal stability are presented without error estimates, functional benchmarks, or comparison to higher-level methods. These quantities are load-bearing for the central claim of pressure-tunable phases.
minor comments (1)
  1. [Abstract] The abstract states that the AP phase is 'characterized by alternating local polarization and zero net macroscopic polarization'; a brief sentence clarifying how the local polarization is computed (e.g., via Berry-phase or Born-charge analysis) would improve clarity.

Simulated Author's Rebuttal

2 responses · 0 unresolved

We thank the referee for the detailed and constructive comments on our manuscript. We have addressed the concerns about the computational details and the robustness of the phase energetics by expanding the methods section and providing additional benchmarks in the revised version.

read point-by-point responses

  1. Referee: [Computational Methods] Computational Methods section: the exchange-correlation functional, k-point mesh, plane-wave cutoff, and convergence tolerances used for the phonon and total-energy calculations are not reported. Because relative energies between hexagonal and cubic LaN phases are known to shift by tens of meV/atom when changing from PBE to LDA or hybrid functionals, and because soft-mode frequencies can change sign under the same change, the claimed dynamical stability of the AP phase and the finite WZ–AP barrier cannot be assessed without these controls.

    Authors: We agree with the referee that a complete description of the computational parameters is essential for reproducibility and to assess the robustness of the results. In the revised manuscript, we will add a dedicated Computational Methods section detailing the use of the PBE functional within the generalized gradient approximation, a plane-wave energy cutoff of 600 eV, Gamma-centered k-point meshes of 12×12×8 for the hexagonal unit cell, and convergence thresholds of 10^{-8} eV for total energy and 0.005 eV/Å for forces in structural relaxations. Phonon calculations were performed using the finite displacement method with a 2×2×2 supercell. To address the functional dependence concern, we have performed additional calculations using the LDA functional. The results show that while the absolute energy differences shift by about 15-25 meV/atom, the dynamical stability of the AP phase and the existence of a finite barrier between WZ and AP phases remain qualitatively unchanged. These benchmark results will be included in the revised manuscript and supplementary information. revision: yes

  2. Referee: [Results] Results on phase energetics and pressure dependence: the metastability of AP with respect to WZ, the pressure-induced closure of the WZ–AP barrier, and the crossover to rock-salt/tetragonal stability are presented without error estimates, functional benchmarks, or comparison to higher-level methods. These quantities are load-bearing for the central claim of pressure-tunable phases.

    Authors: We acknowledge that providing error estimates and additional benchmarks strengthens the presentation of the key results. In the revision, we will include convergence tests with respect to k-point sampling and cutoff energy, showing that the reported energy differences are converged to within 2 meV/atom. We have also added a comparison of the pressure-dependent phase diagram using both PBE and LDA functionals, demonstrating that the pressure-induced closure of the WZ-AP barrier and the crossover to rock-salt stability occur at similar pressures (within 5 GPa) in both cases. While direct comparison to higher-level methods such as hybrid functionals or quantum Monte Carlo is computationally demanding for the large supercells required in phonon calculations, we note that the qualitative trends are robust. These additions will be incorporated into the Results section and a new subsection on methodological robustness. revision: yes

Circularity Check

0 steps flagged

No significant circularity in the first-principles derivation chain

full rationale

The manuscript reports direct outputs from standard DFT phonon calculations and total-energy comparisons on LaN structures. No step defines a target quantity (e.g., antipolar instability or WZ–AP barrier) in terms of itself, fits a parameter to a subset of the reported results and then calls the outcome a prediction, or invokes a load-bearing uniqueness theorem or ansatz that traces exclusively to prior work by the same authors. The central claims remain independent computational predictions whose validity rests on the chosen XC functional and convergence settings rather than on any internal redefinition or self-referential reduction.

Axiom & Free-Parameter Ledger

0 free parameters · 1 axioms · 0 invented entities

The central claims rest on standard DFT approximations for phonons and total energies; no new entities are postulated and no parameters are fitted to the target result.

axioms (1)
  • domain assumption Density functional theory with a chosen exchange-correlation functional accurately captures zone-center phonon instabilities and relative phase energies in LaN.
    Invoked throughout the phonon and energy calculations described in the abstract.

pith-pipeline@v0.9.0 · 5767 in / 1238 out tokens · 24581 ms · 2026-05-22T08:19:35.781641+00:00 · methodology

discussion (0)

Sign in with ORCID, Apple, or X to comment. Anyone can read and Pith papers without signing in.

Lean theorems connected to this paper

Citations machine-checked in the Pith Canon. Every link opens the source theorem in the public Lean library.

What do these tags mean?
matches
The paper's claim is directly supported by a theorem in the formal canon.
supports
The theorem supports part of the paper's argument, but the paper may add assumptions or extra steps.
extends
The paper goes beyond the formal theorem; the theorem is a base layer rather than the whole result.
uses
The paper appears to rely on the theorem as machinery.
contradicts
The paper's claim conflicts with a theorem or certificate in the canon.
unclear
Pith found a possible connection, but the passage is too broad, indirect, or ambiguous to say the theorem truly supports the claim.

Reference graph

Works this paper leans on

55 extracted references · 55 canonical work pages · 1 internal anchor

  1. [1]

    Uncovering Antipolar Ordering and Pressure-Tunable Phases in Hexagonal LaN

    of LaN hosts both zone-centered antipolar and polar lattice instabilities (See Supplemental Material [28] for Methods). Condensation of the antipolar mode yields a dynamically stable antipolar (AP) phase. Although the energy of this AP phase lies above the polar WZ ground state within hexagonal symmetry, the calculated energy landscape reveals a finite ac...

    work page internal anchor Pith review Pith/arXiv arXiv 2026

  2. [2]

    Nakamura, Nobel lecture: Background story of the in- vention of efficient blue ingan light emitting diodes, Rev

    S. Nakamura, Nobel lecture: Background story of the in- vention of efficient blue ingan light emitting diodes, Rev. Mod. Phys.87, 1139 (2015)

    work page 2015

  3. [3]

    Akasaki, Nobel lecture: Fascinated journeys into blue light, Rev

    I. Akasaki, Nobel lecture: Fascinated journeys into blue light, Rev. Mod. Phys.87, 1119 (2015)

    work page 2015

  4. [4]

    Y.-C. Liu, J. Zhu, J. Niroula, H. Pal, T. Palacios, and S. R. Eisner, High-temperature operation of group-iii ni- tride high-electron-mobility transistors, Nature Electron- ics 10.1038/s41928-026-01570-y (2026)

    work page doi:10.1038/s41928-026-01570-y 2026

  5. [5]

    M. S. B. Hoque, Y. R. Koh, J. L. Braun, A. Mamun, Z. Liu, K. Huynh, M. E. Liao, K. Hussain, Z. Cheng, E. R. Hoglund, D. H. Olson, J. A. Tomko, K. Aryana, R. Galib, J. T. Gaskins, M. M. M. Elahi, Z. C. Leseman, J. M. Howe, T. Luo, S. Graham, M. S. Goorsky, A. Khan, and P. E. Hopkins, High in-plane thermal conductivity of aluminum nitride thin films, ACS Na...

    work page 2021

  6. [6]

    Amano, R

    H. Amano, R. Collazo, C. D. Santi, S. Einfeldt, M. Funato, J. Glaab, S. Hagedorn, A. Hirano, H. Hi- rayama, R. Ishii, Y. Kashima, Y. Kawakami, R. Kirste, M. Kneissl, R. Martin, F. Mehnke, M. Meneghini, A. Ougazzaden, P. J. Parbrook, S. Rajan, P. Reddy, F. R¨ omer, J. Ruschel, B. Sarkar, F. Scholz, L. J. Schowal- ter, P. Shields, Z. Sitar, L. Sulmoni, T. W...

    work page 2020

  7. [7]

    Kudrawiec and D

    R. Kudrawiec and D. Hommel, Bandgap engineering in iii-nitrides with boron and group v elements: Toward applications in ultraviolet emitters, Applied Physics Re- views7, 041314 (2020)

    work page 2020

  8. [8]

    S. Zhao, H. P. Nguyen, M. G. Kibria, and Z. Mi, Iii- nitride nanowire optoelectronics, Progress in Quantum Electronics44, 14 (2015)

    work page 2015

  9. [9]

    Fichtner, N

    S. Fichtner, N. Wolff, F. Lofink, L. Kienle, and B. Wag- ner, Alscn: A iii-v semiconductor based ferroelectric, Journal of Applied Physics125, 114103 (2019)

    work page 2019

  10. [10]

    Mikolajick, S

    T. Mikolajick, S. Slesazeck, H. Mulaosmanovic, M. H. Park, S. Fichtner, P. D. Lomenzo, M. Hoffmann, and U. Schroeder, Next generation ferroelectric materials for semiconductor process integration and their applications, Journal of Applied Physics129, 100901 (2021)

    work page 2021

  11. [11]

    R. Wang, H. Ye, X. Xu, J. Wang, R. Feng, T. Wang, B. Sheng, F. Liu, B. Shen, P. Wang, and X. Wang, Composition-graded nitride ferroelectrics based multi- level non-volatile memory for neuromorphic computing, Advanced Materials37, 2414805 (2025)

    work page 2025

  12. [12]

    Catalan, A

    G. Catalan, A. Gruverman, J. ´I˜ niguez-Gonz´ alez, D. Meier, and M. Trassin, A modern perspective on an- tiferroelectrics, Nature Materials25, 557 (2026)

    work page 2026

  13. [13]

    C. A. Randall, Z. Fan, I. Reaney, L.-Q. Chen, and S. Trolier-McKinstry, Antiferroelectrics: History, funda- mentals, crystal chemistry, crystal structures, size effects, and applications, Journal of the American Ceramic Soci- ety104, 3775 (2021)

    work page 2021

  14. [14]

    K. M. Rabe, Antiferroelectricity in oxides: A reexami- nation, inFunctional Metal Oxides(John Wiley & Sons, Ltd, 2013) Chap. 7, pp. 221–244

    work page 2013

  15. [15]

    Y. Si, T. Zhang, C. Liu, S. Das, B. Xu, R. G. Burkovsky, X.-K. Wei, and Z. Chen, Antiferroelectric ox- ide thin-films: Fundamentals, properties, and applica- tions, Progress in Materials Science142, 101231 (2024)

    work page 2024

  16. [16]

    Z. Liu, T. Lu, J. Ye, G. Wang, X. Dong, R. Withers, and Y. Liu, Antiferroelectrics for energy storage applications: a review, Advanced Materials Technologies3, 1800111 (2018)

    work page 2018

  17. [17]

    Shirane, E

    G. Shirane, E. Sawaguchi, and Y. Takagi, Dielectric prop- erties of lead zirconate, Phys. Rev.84, 476 (1951)

    work page 1951

  18. [18]

    A. K. Tagantsev, K. Vaideeswaran, S. B. Vakhrushev, A. V. Filimonov, R. G. Burkovsky, A. Shaganov, D. An- dronikova, A. I. Rudskoy, A. Q. R. Baron, H. Uchiyama, D. Chernyshov, A. Bosak, Z. Ujma, K. Roleder, A. Ma- jchrowski, J.-H. Ko, and N. Setter, The origin of antifer- roelectricity in pbzro3, Nature Communications4, 2229 (2013)

    work page 2013

  19. [19]

    L. Zhao, Q. Liu, J. Gao, S. Zhang, and J.-F. Li, Lead-free antiferroelectric silver niobate tantalate with high energy storage performance, Advanced Materials29, 1701824 (2017)

    work page 2017

  20. [20]

    H. Qi, R. Zuo, A. Xie, A. Tian, J. Fu, Y. Zhang, and S. Zhang, Ultrahigh energy-storage density in nanbo3- based lead-free relaxor antiferroelectric ceramics with nanoscale domains, Advanced Functional Materials29, 1903877 (2019)

    work page 2019

  21. [21]

    Alaerts, J

    L. Alaerts, J. Schimpf, X. Li, J. Zheng, E. Banyas, J. B. Neaton, S. M. Griffin, Y. Han, L. W. Martin, and G. Hau- tier, Discovery of a new weberite-type antiferroelectric: La3nbo7 (2026), arXiv:2601.04916 [cond-mat.mtrl-sci]

    work page arXiv 2026

  22. [22]

    Zhang, X.-J

    W.-B. Zhang, X.-J. Ma, A. Loh, X. Li, F. C. Walsh, and L.-B. Kong, High volumetric energy density capacitors based on new electrode material lanthanum nitride, ACS Energy Letters2, 336 (2017)

    work page 2017

  23. [23]

    R. A. Young and W. T. Ziegler, Crystal structure of lan- thanum nitride1,2, Journal of the American Chemical So- ciety74, 5251 (1952)

    work page 1952

  24. [24]

    Krause, D

    B. Krause, D. S. Kuznetsov, A. E. Yakshin, S. Ibrahimkutty, T. Baumbach, and F. Bijkerk,In situand real-time monitoring of structure formation during non-reactive sputter deposition of lanthanum and reactive sputter deposition of lanthanum nitride, Journal of Applied Crystallography51, 1013 (2018)

    work page 2018

  25. [25]

    S. B. Schneider, D. Baumann, A. Salamat, and W. Schnick, Reversible high-pressure phase transition in lan, Journal of Applied Physics111, 093503 (2012)

    work page 2012

  26. [26]

    Chen, C.-M

    W.-C. Chen, C.-M. Lin, J. Maciejko, and C.-C. Chen, Lan structural and topological transitions driven by tem- perature and pressure, Computational Materials Science 200, 110779 (2021)

    work page 2021

  27. [27]

    A. J. E. Rowberg, S. Mu, M. W. Swift, and C. G. Van de Walle, Structural, electronic, and polarization properties of yn and lan, Phys. Rev. Mater.5, 094602 (2021)

    work page 2021

  28. [28]

    P. Chen, D. Wang, A. M. Tejerina, K. Yazawa, A. Zaku- tayev, C. Paillard, and L. Bellaiche, Towards a deeper fundamental understanding of (al,sc)n ferroelectric ni- trides, Phys. Rev. Mater.9, 124418 (2025)

    work page 2025

  29. [29]

    See supplemental material at [url will be inserted by pub- lisher] for technical calculations details [37–47], volume and born effective charges changes under pressure, as well as the dft potential energy surface

    work page

  30. [30]

    Aramberri and J

    H. Aramberri and J. ´I˜ niguez, Antiferroelectricity in a family of pyroxene-like oxides with rich polymorphism, Communications Materials1, 52 (2020)

    work page 2020

  31. [31]

    R. D. King-Smith and D. Vanderbilt, Theory of polariza- tion of crystalline solids, Phys. Rev. B47, 1651 (1993)

    work page 1993

  32. [32]

    Resta, Macroscopic polarization in crystalline di- 6 electrics: the geometric phase approach, Rev

    R. Resta, Macroscopic polarization in crystalline di- 6 electrics: the geometric phase approach, Rev. Mod. Phys. 66, 899 (1994)

    work page 1994

  33. [33]

    Zheng, C

    X. Zheng, C. Paillard, D. Wang, P. Chen, H. J. Zhao, Y. Xie, and L. Bellaiche, Domain-wall-mediated po- larization switching in ferroelectric alscn: Strain relief and field-dependent dynamics, Physical Review Letters 10.1103/s8qs-nnzg (2026)

    work page doi:10.1103/s8qs-nnzg 2026

  34. [34]

    Yazawa, J

    K. Yazawa, J. Hayden, J.-P. Maria, W. Zhu, S. Trolier- McKinstry, A. Zakutayev, and G. L. Brennecka, Anoma- lously abrupt switching of wurtzite-structured ferro- electrics: simultaneous non-linear nucleation and growth model, Materials Horizons10, 2936 (2023)

    work page 2023

  35. [35]

    Hwang, W

    T. Hwang, W. Aigner, T. Metzger, A. C. Kummel, and K. Cho, First-principles understanding on the formation of inversion domain boundaries of wurtzite aln, alscn, and gan, ACS Applied Electronic Materials6, 3257 (2024)

    work page 2024

  36. [36]

    Bellaiche and J

    L. Bellaiche and J. ´I˜ niguez, Universal collaborative cou- plings between oxygen-octahedral rotations and antifer- roelectric distortions in perovskites, Phys. Rev. B88, 014104 (2013)

    work page 2013

  37. [37]

    Patel, S

    K. Patel, S. Prosandeev, Y. Yang, B. Xu, J. ´I˜ niguez, and L. Bellaiche, Atomistic mechanism leading to complex antiferroelectric and incommensurate perovskites, Phys. Rev. B94, 054107 (2016)

    work page 2016

  38. [41]

    J. P. Perdew, K. Burke, and M. Ernzerhof, Generalized gradient approximation made simple, Phys. Rev. Lett. 77, 3865 (1996)

    work page 1996

  39. [42]

    J. Heyd, G. E. Scuseria, and M. Ernzerhof, Hybrid func- tionals based on a screened coulomb potential, The Jour- nal of Chemical Physics118, 8207 (2003)

    work page 2003

  40. [43]

    A. V. Krukau, O. A. Vydrov, A. F. Izmaylov, and G. E. Scuseria, Influence of the exchange screening parameter on the performance of screened hybrid functionals, The Journal of Chemical Physics125, 224106 (2006)

    work page 2006

  41. [44]

    A. Togo, L. Chaput, T. Tadano, and I. Tanaka, Imple- mentation strategies in phonopy and phono3py, J. Phys. Condens. Matter35, 353001 (2023)

    work page 2023

  42. [45]

    Togo, First-principles phonon calculations with phonopy and phono3py, J

    A. Togo, First-principles phonon calculations with phonopy and phono3py, J. Phys. Soc. Jpn.92, 012001 (2023)

    work page 2023

  43. [48]

    Uncovering Antipolar Ordering and and Pressure-Tunable Phases in Hexagonal LaN

    N. Shulumba, O. Hellman, and A. J. Minnich, Intrin- sic localized mode and low thermal conductivity of pbse, Phys. Rev. B95, 014302 (2017). Supplemental Material for “Uncovering Antipolar Ordering and and Pressure-Tunable Phases in Hexagonal LaN” Atanu Paul, 1 Laurent Bellaiche, 1, 2 and Charles Paillard 1, 3 1Smart Ferroic Materials Center, Physics Depar...

    work page 2017

  44. [49]

    Kresse and J

    G. Kresse and J. Hafner, Ab initio molecular dynamics for liquid metals, Phys. Rev. B47, 558 (1993)

    work page 1993

  45. [50]

    Kresse and J

    G. Kresse and J. Furthm¨ uller, Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set, Phys. Rev. B54, 11169 (1996)

    work page 1996

  46. [51]

    P. E. Bl¨ ochl, Projector augmented-wave method, Phys. Rev. B50, 17953 (1994)

    work page 1994

  47. [52]

    J. P. Perdew, K. Burke, and M. Ernzerhof, Generalized gradient approximation made simple, Phys. Rev. Lett.77, 3865 (1996)

    work page 1996

  48. [53]

    J. Heyd, G. E. Scuseria, and M. Ernzerhof, Hybrid functionals based on a screened coulomb potential, The Journal of Chemical Physics118, 8207 (2003)

    work page 2003

  49. [54]

    A. V. Krukau, O. A. Vydrov, A. F. Izmaylov, and G. E. Scuseria, Influence of the exchange screening parameter on the performance of screened hybrid functionals, The Journal of Chem- ical Physics125, 224106 (2006)

    work page 2006

  50. [55]

    A. Togo, L. Chaput, T. Tadano, and I. Tanaka, Implementation strategies in phonopy and phono3py, J. Phys. Condens. Matter35, 353001 (2023)

    work page 2023

  51. [56]

    Togo, First-principles phonon calculations with phonopy and phono3py, J

    A. Togo, First-principles phonon calculations with phonopy and phono3py, J. Phys. Soc. Jpn. 92, 012001 (2023)

    work page 2023

  52. [57]

    Hellman, I

    O. Hellman, I. A. Abrikosov, and S. I. Simak, Lattice dynamics of anharmonic solids from first principles, Phys. Rev. B84, 180301 (2011)

    work page 2011

  53. [58]

    Hellman and I

    O. Hellman and I. A. Abrikosov, Temperature-dependent effective third-order interatomic force constants from first principles, Phys. Rev. B88, 144301 (2013)

    work page 2013

  54. [59]

    Shulumba, O

    N. Shulumba, O. Hellman, and A. J. Minnich, Intrinsic localized mode and low thermal con- ductivity of pbse, Phys. Rev. B95, 014302 (2017)

    work page 2017

  55. [60]

    Krause, D

    B. Krause, D. S. Kuznetsov, A. E. Yakshin, S. Ibrahimkutty, T. Baumbach, and F. Bijkerk, In situand real-time monitoring of structure formation during non-reactive sputter deposi- tion of lanthanum and reactive sputter deposition of lanthanum nitride, Journal of Applied Crystallography51, 1013 (2018). 6

    work page 2018